Título : Degradación térmica de polimetíl metacrilato en múltiples extrusiones
Otros títulos: Thermal degradation of polymethyl methacrylate in multiple extrusions
Autores: Rojas, Andrés F.
Aranzazu, Laura M.
Gaviria, Guillermo H.
Carrero, Javier I.
Palabras clave : Degradación térmica de polímeros
múltiples extrusiones
triplete cinético
Multiple extrusions
thermal degradation of polymers
triplet kinetic
Fecha de publicación: 21-may-2015
Resumen: Resumen Se presentan los resultados del estudio cinético de la degradación térmica del Polimetíl Metacrilato – PMMA, tanto virgen como procesado por extrusión hasta cinco ciclos de reprocesamiento, en una extrusora monohusillo. Después de cada reprocesamiento se tomó una muestra para análisis. A estas muestras se les determinó la temperatura de transición vítrea (por DSC), índice de fluidez y la temperatura máxima de pérdida de peso (por TGA). Los resultados del análisis termogravimétrico se utilizaron para determinar el triplete cinético por medio de métodos isoconversionales, no isoconversionales, y dinámicos. Se encontró que las curvas TG, DTG y de conversión, se desplazan a la derecha al aumentar la velocidad de calentamiento. También se encontró que los métodos no isoconversionales diferenciales presentaron valores de energía de activación mayores a los métodos integrales. La energía de activación aumentó con el reprocesamiento y la probabilidad o fracción de colisión aumenta con la velocidad de calentamiento. Abstract This work presents a kinetic study of thermal degradation of polymethyl metacrylate (PMMA). This material was subject of five extrusion cycles in a single barrel screw extruder, and results for raw and reprocessed material are presented. Glass transition temperature (by DSC), melt flow index, and temperature of maximum weight loss rate (by TGA) were determined in samples taken after each reprocessing. Results from thermogravimetric analysis were used to get the kinetic triplet by isoconversional, non-isoconversional, and dynamic methods as it is reported in literature. It was found that heating shifts to the right TG, DTG, and conversion curves. Activation energy values found with non-isoconversional differential methods tend to be higher than those found with integral methods. Also the activation energy increased with reprocessing, while the probability or collision factor increased with the heating rate.
URI: http://hdl.handle.net/10893/8490
Aparece en las colecciones: Vol. 16 no. 2, 2014 / Ingeniería y Competitividad

Texto completo:

Archivo Descripción Tamaño Formato
Degradacion termica de polimetil.pdf1.15 MBAdobe PDFDescargar aquí
Ver estadísticas

Los ítems de Biblioteca Digital están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.

 

Biblioteca Mario Carvajal
biblioteca@univalle.edu.co
Teléfonos +57 2 3212950 - Fax 3212977
Universidad del Valle - Ciudad Universitaria
Calle 13 # 100-00 Cali, Colombia
    Biblioteca San Fernando
biblioteca@univalle.edu.co
Teléfonos +57 2 5185633 - Fax 5581951
Universidad del Valle - Sede San Fernando
Calle 4a.B # 36-00
Cali, Colombia
    Biblioteca Colección Clínica
biblioteca@univalle.edu.co
Teléfonos +57 2 5576113
Hospital Universitario del Valle
Calle 5a # 36-08
Cali, Colombia
DSpace Software Copyright © 2002-2008 MIT and Hewlett-Packard