Título : Estudio de morteros adicionados con catalizador usado de craqueo catalítico (FCC) bajo el efecto de altas temperaturas
Otros títulos: Study of mortars added with fluid catalytic cracking catalyst residue (FCC) under the influence of high temperatures
Autores: Izquierdo, Silvia R.
Mejía de Gutiérrez, Ruby
Torres Agredo, Janneth
Palabras clave : Altas temperaturas
catalizador de craqueo catalítico
microestructura
morteros de cemento adicionado
resistencia mecánica residual
Blended cement mortars
catalytic cracking catalyst
high temperature
microstructure
residual mechanical strength
Fecha de publicación: 22-may-2015
Resumen: RESUMEN Se analizó el efecto de la incorporación de un residuo de la industria petroquímica, denominado catalizador gastado del craqueo catalítico (FCC), en pastas y morteros expuestos a temperaturas de 25ºC, 200ºC, 300ºC, 500ºC, 750ºC, 1000ºC y 1200ºC, utilizando como materiales de referencia, además del cemento Portland (OPC), metacaolín (MK) y humo de sílice (HS). Las adiciones fueron incorporadas en un 10% con respecto a la cantidad de cemento. Se evaluó el efecto de la temperatura de exposición en el peso y resistencia a la compresión, igualmente las modificaciones en el aspecto físico posterior a la exposición térmica. Se realizaron análisis termogravimétricos (TG) y de microscopía electrónica de barrido (SEM), para evidenciar los cambios. Los resultados indican que el FCC actúa positivamente. Se resalta que a temperatura de 750ºC la resistencia residual de los morteros de OPC es un 16,53% de la resistencia a temperatura ambiente, comparado a los morteros adicionados, los cuales alcanzan hasta un 29,24%. El FCC retrasa la aparición de grietas en los elementos expuestos a altas temperaturas comparados a aquellos sin adición; su resistencia residual a 750°C es un 26% superior al material de referencia (OPC). ABSTRACT In this article, the effect of the addition of a petrochemical industry residue, called spent catalyst from the catalytic cracking (FCC), in cementitious materials exposed to temperatures of 25 °C, 200 °C, 300 °C, 500 °C, 750 °C, 1000 °C and 1200 °C was analyzed. Metakaolin (MK) and silica fume (HS) were used as reference materials. The additions were incorporated into a 10% replacement of the proportion of cement (OPC) in the mixture. The effects of temperature exposure in the weight change and compressive strength were evaluated. Also, changes in the physical appearance of the specimens after thermal exposure were studied. Techniques of Thermogravimetric Analysis (TG) and scanning electron microscopy (SEM) were used to analyze the changes. The results indicate that the addition of the FCC acts positively on the performance of Portland cement. It is noteworthy that the residual strength of OPC mortars at temperature of 750 °C is 16.53% of the strength at room temperature compared to the mortars added, which reach up to 29.24%. The FCC addition delayed the appearance of cracks in the elements exposed to high temperatures compared to those without addition; its residual strength at 750°C is 26% higher than the reference material (OPC).
URI: http://hdl.handle.net/10893/8505
Aparece en las colecciones: Vol. 16 no. 2, 2014 / Ingeniería y Competitividad

Texto completo:

Archivo Descripción Tamaño Formato
estudio de morteros.pdf1.72 MBAdobe PDFDescargar aquí
Ver estadísticas

Los ítems de Biblioteca Digital están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.

 

Biblioteca Mario Carvajal
biblioteca@univalle.edu.co
Teléfonos +57 2 3212950 - Fax 3212977
Universidad del Valle - Ciudad Universitaria
Calle 13 # 100-00 Cali, Colombia
    Biblioteca San Fernando
biblioteca@univalle.edu.co
Teléfonos +57 2 5185633 - Fax 5581951
Universidad del Valle - Sede San Fernando
Calle 4a.B # 36-00
Cali, Colombia
    Biblioteca Colección Clínica
biblioteca@univalle.edu.co
Teléfonos +57 2 5576113
Hospital Universitario del Valle
Calle 5a # 36-08
Cali, Colombia
DSpace Software Copyright © 2002-2008 MIT and Hewlett-Packard